Plexiglas® Satinice df22 zk6BR

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nWMtH0_Plexiglas-Satinice-df22-zk6BR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PLEXIGLAS® Satinice df22 zk6BR, based on PLEXIGLAS® Resist zk6BR, is an impact modified molding compound characterized by diffuse scattering of light.

Typical properties of impact modified PLEXIGLAS® molding compound are

high break resistance and impact strength

improved resistance to stress cracking

good weather resistance

high surface hardness and mar resistance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Satinice df22 zk6BR is characterized by the following special properties:

very good lightdiffusion combined with excellent light transmission

matte surfaces can be obtained by varying the extrusion parameters.

Application:
Used for extruding profiles and sheets, but also for injection molding items for lighting engineering applications

Examples:
applications that call for light diffusion combined with optimum transmission

General Information
Additive	Impact Modifier
Features	Good Weather Resistance High ESCR (Stress Crack Resist.) High Hardness High Impact Resistance High Strength Light Stabilized
Uses	Lighting Diffusers Profiles Sheet
Forms	Pellets
Processing Method	Extrusion Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.15	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	1.40	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1800	MPa	ISO 527-2/1
Tensile Stress (Yield)	45.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	40	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.5	kJ/m²	ISO 179/1
Charpy Unnotched Impact Strength (23°C)	54	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	99.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	93.0	°C	ISO 75-2/A
Glass Transition Temperature	109	°C	ISO 11357-2
Vicat Softening Temperature	98.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	9.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	700	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Additional Information	Nominal Value	Unit	Test Method
Half-Value Angle	12.5	°	DIN 5036

Optical	Nominal Value	Unit	Test Method
Transmittance ¹	86.0	%	ISO 13468-2

Extrusion	Nominal Value	Unit
Drying Temperature	< 85.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	230 to 260	°C
Die Temperature	260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Purell PE 2420 F	LyondellBasell Industries	LDPE	Purell
Karina CRYSTAL COMPOUND (SP31483) -E 65/275-NT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
PHOENIX™ 2551	Phon Tech Industrial Company	SEBS	PHOENIX™
Hostacom HBC 308L W92607	LyondellBasell Industries	PP Homopolymer	Hostacom
Dryflex® SE 55A301	ELASTO	TPE	Dryflex®