Starex NH-0825 S
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nVWZkU_StarexNH0825S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex NH-0825 S is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The application areas of Starex NH-0825 S include housing and commercial/office supplies. The main features are: flame retardant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 105 | ASTM D785 | |
| R scale | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 41.0 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 2300 | MPa | ASTM D790 |
| -- 3 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 63.0 | MPa | ASTM D790 |
| -- 5 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| 23°C 6 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 93.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 210 - 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-2009S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DIOSHY® LP-855 | DIOSHY Co.,Ltd. | SEBS+SBS | DIOSHY® |
| LNP™ STAT-KON™ OX00428 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ RF007SXQ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| OmniTech™ ABS GR10 | OMNI Plastics, LLC | ABS | OmniTech™ |