GELOY™ CR3020 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nVSoGd_GELOYCR3020resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low-gloss ASA for profile and capstock applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 5.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 6.4 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.55 - 0.63 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1840 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 30.0 | MPa | ASTM D638 |
| Fracture | 31.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/50 |
| Fracture 5 | 38 | % | ASTM D638 |
| Fracture | 23 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1860 | MPa | ASTM D790 |
| -- 7 | 1800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 56.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 57.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 1.2 | J/m | ASTM D256 |
| 23°C | 8.4 | J/m | ASTM D256 |
| -30°C 9 | 3.8 | kJ/m² | ISO 180/1A |
| 23°C 10 | 26 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 4.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 74.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 77.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50, ASTM D1525 12 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Cylinder Zone 1 Temp. | 204 - 216 | °C | |
| Cylinder Zone 2 Temp. | 216 - 232 | °C | |
| Cylinder Zone 3 Temp. | 221 - 238 | °C | |
| Cylinder Zone 4 Temp. | 227 - 243 | °C | |
| Adapter Temperature | 227 - 243 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 227 - 243 | °C | |
| Calibration Temp, First | 15.6 - 65.6 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 12 hrsMinimum Moisture Content: .02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8600FR | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| AMPLIFY™ GR 209 | The Dow Chemical Company | MAH-g | AMPLIFY™ GR |
| LNP™ THERMOCOMP™ UCF22S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Sylvin 9067-90 LMW Grey 9368 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Toyolac® 100G-20 | Toray Resin Company | ABS | Toyolac® |