CERTENE™ LDF-0220B
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nSPMQ0_CERTENE-LDF-0220B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-0220B is a certified prime resin specially designed for production of heavy duty Blown films for industrial applications requiring excellent mechanical properties, such as heavy duty sacks, shipping bags, shrink wrapped pallet hoods, construction, agriculture and greenhouses. LDF-0220B features easy processability and films exhibit high toughness, high impact and tear strength, and excellent shrinkage properties. Minimum recommended film thickness is 2.5 mils. LDF-0220B contains no slip and medium antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm | 173 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 13.0 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 13.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 32.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 200 | % | ASTM D882 |
| TD : Fracture, 51 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 260 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 600 | g | ASTM D1922 |
| TD : 51 µm | 150 | g | ASTM D1922 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V33 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Wellamid® 42LH XE-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Hifax CB247 | LyondellBasell Industries | TPO (POE) | Hifax |
| TOTAL Polyethylene Aceso® PEM 1870 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Sylvin 9771-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |