TAROLOX 10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nQW8wV_TAROLOX-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT medium viscosity, very good resistance to chemical agents, good flow, good mechanical and thermal properties. Available: all colours, heat stabilised (H), release agent (W), fast cycles (S). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 to 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/1.2 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 to 1.8 | % | |
| Across Flow | 1.6 to 1.8 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.080 | % | ASTM D570, ISO 62 |
| Saturation | 0.50 | % | ASTM D570 |
| Saturation, 23°C | 0.50 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Elongation (Break) | > 100 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 80.0 | MPa | ISO 178 |
| -- 2 | 70.0 | MPa | ISO 178 |
| Yield | 80.0 | MPa | ASTM D790 |
| Break | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 6.0 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -20°C, 3.20 mm | 30 | J/m | |
| 23°C, 3.20 mm | 50 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 160 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 4 | 90.0 | °C | |
| -- 5 | 120 | °C | |
| -- 6 | 130 | °C | |
| -- 7 | 160 | °C | |
| Vicat Softening Temperature | |||
| -- | 200 | °C | ASTM D1525, ISO 306/A50 9 8 |
| -- | 180 | °C | ASTM D1525, ISO 306/B50 10 9 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 to 225 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | > 600 | V | |
| Solution B | 350 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 20000 hrs |
| 5 . | Heat Stabilized, 20000 hrs |
| 6 . | Short Term |
| 7 . | Heat Stabilized, Short Term |
| 8 . | Rate A (50°C/h), Loading 1 (10 N) |
| 9 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1782 | RTP Company | PPE | RTP |
| UNISOFT TPE™ ST-78A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Cheng Yu B610 | Cheng Yu Plastic Company Limited | PC+PBT | Cheng Yu |
| Elastron® TPO T401.D32.N | Elastron USA, Inc. | TPO (POE) | Elastron® TPO |
| TECHNYL® A 60G1 V30 BLACK 61 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |