EPLAMID 66 IMP NC C001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nQ1sYs_EPLAMID-66-IMP-NC-C001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced and modified polyamide 66, with improved good-impact resistance, heat stabilized, lubricated for injection molding. Eplamid 66 IMP offers an excellent Notched High Impact resistance with ensures outstanding performance at low temperatures making it suitable for all sectors of industries and for applications such as sports & liesure and automative industries. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.8 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 1.6 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 76 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | 1650 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 42.0 | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 50 | > 30 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1800 | 1550 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 92.0 | 82.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 72 | 76 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 70 | 75 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 248 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 280 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiprene® 4045 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| SOLLAMID B 2700 FV 35 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| NEXT SIGNATURE POMC HF-300 | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT SIGNATURE |
| Mytex® 8224(L)(W) | Mytex Polymers | PP, Unspecified | Mytex® |
| Karina GRAY PVC COMPOUND 853-18/323-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |