TECHNYL® C 218 MZ20 V10 BLACK Z
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nPGlVL_TECHNYL-C-218-MZ20-V10-BLACK-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA6, reinforced 20 % mineral filler and 10 % of glass fibre, heat stabilized, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.95 | -- | % | |
| Flow | 0.54 | -- | % | |
| Molding Shrinkage Isotropy | 0.570 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7400 | 4500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 100 | 60.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.3 | 5.5 | % | ISO 527-2/1A |
| Flexural Modulus | 9300 | -- | MPa | ISO 178 |
| Flexural Stress | 255 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 14 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 60 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 15 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | -- | 82 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REMAFIN® Polyolefin Color Masterbatch | Clariant Corporation | TP, Unspecified | REMAFIN® |
| VINIKA® CA88NA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Ultraform® W 2320 0035 LEV | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Nylene® Mach 6 | Custom Resins Group | Nylon 6 | Nylene® |
| ADENE® O07MQE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |