LNP™ STAT-KON™ RX10004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nP4An0_LNP-STAT-KON-RX10004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RX10004 is a compound based on PA66 resin, containing Glass Fiber and Carbon Fiber. Added features are: Electrically Conductive, Easy Molding Also known as: LNP* STAT-KON* Compound RX10004 Product reorder name: RX10004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 230 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16900 | MPa | ISO 178 |
| Flexural Stress | 334 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 93 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+7 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 54 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Siloxane Masterbatch MB50-011 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| TABOREN PH 92 H 15 | SILON s.ro | PP Homopolymer | TABOREN |
| ALTECH® PA66 A 1000/109 GY1010-07LS | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Armlen® PP TM 40-1M | Poly Plastic | PP, Unspecified | Armlen® |