Oleflex鈩?6750-70A-0000 Natural, 815179C
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Oleflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nMizUx_Oleflex-6750-70A-0000-Natural-815179C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Oleflex™6750-70A-0000 Natural, 815179C is a thermoplastic elastomer (TPE) material,. This product is available in North America,. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shao A, mm) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5A | ||
| 2.00 mm | 2.10 | MPa | ISO 527-2/5A |
| 70°C, 2.00 mm 1 | 2.70 | MPa | ISO 527-2/5A |
| Tensile Strain | ISO 527-2/5A | ||
| Fracture, 2.00mm | 340 | % | ISO 527-2/5A |
| Fracture, 70°C, 2.00mm 2 | 680 | % | ISO 527-2/5A |
| Wear resistance (mm) 3 | 7869 | SAE J948 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold flexibility- High and Low Bend Test | |||
| -30°C, 2.54 cm | Pass | ||
| -24°C, 2.54 cm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Combustibility (mm) | 27 | mm/min | FMVSS 302 |
| Atomization (mm) 4 | 99.0 | SAE J1756 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Surface Temperature - Heat Resistance (85°C, 2.00 mm) 5 | 5.00 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (2.00 mm) | 16.6 | kN/m | ASTM D624 |
| Compression Set | |||
| 70°C, 7 hr | 56 | % | ASTM D395 |
| 70°C, 22 hr | 67 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Hot Odor Test, SAE J1351: 1.4 |
| Note Message | |
|---|---|
| 1 . | After 7 h @ 70°C |
| 2 . | After 7 h @ 70°C |
| 3 . | Tested according to SAE J948/ASTM D3884 |
| 4 . | Method B |
| 5 . | 168 h @ 85°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake HDPE MC2004 | Westlake Chemical Corporation | HDPE | Westlake HDPE |
| BESTNYL SI00VI01BWX | Triesa Plastics | Nylon 6 | BESTNYL |
| FORMULA P 9002 | Putsch Kunststoffe GmbH | PP Copolymer | FORMULA P |
| Geon™ Vinyl Wire & Cable W780L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| LNP™ THERMOCOMP™ 4X08423 compound | SABIC Innovative Plastics | PFA | LNP™ THERMOCOMP™ |