Duron PEI 4001
| Category: | PEI , Polyether Imide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nMMGHm_Duron-PEI-4001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PEI 4001 is a glass filled polyetherimide resin designed for wear resistance and reduced friction. It offers a superior combination of mechanical, electrical, and thermal properties. It provides outstanding processability and good chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 125 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 195 | °C | ASTM D648 |
| Vicat Softening Temperature | 208 | °C | ASTM D1525 |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 10 kJ/m²Unnotched Izod Impact, ASTM D256: 50 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 R2 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| TOTAL Polystyrene Compound 827 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Fainplast PVC KL 95 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ THERMOTUF™ WF006I compound | SABIC Innovative Plastics | PBT | LNP™ THERMOTUF™ |
| POTICON NT863 | Otsuka Chemical Co., Ltd. | Nylon, Unspecified | POTICON |