Lupos庐 HR2207A
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLfZMM_Lupos-HR2207A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, Heat Resistance Application Electric & Electronic (Housing, Components) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 5880 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, 6.40 mm) | 105 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 235 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 245 | °C | |
| Processing (Melt) Temp | 235 to 245 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 18.6kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3405 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| TRIBIT® 1800M30 | Samyang Corporation | PBT | TRIBIT® |
| Borstar® HE6068 | Borealis AG | HDPE | Borstar® |
| Plexiglas® Satinice df23 8N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| PENTAMID B H TF25 black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |