RIALFILL C 15 S 15 C3
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLaTq4_RIALFILL-C-15-S-15-C3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer copound, 15% filled with calcium carbonate, base thermal stabilization. High flowability rate for injection molding. Available in versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 1.3 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Acetaldehyde (150°C) | 6.3 | day | ISO 4577 |
| Ash Content | 15 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 69 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 15.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 6.0 | % | |
| Break, 23°C | 350 | % | |
| Flexural Modulus 2(23°C) | 1300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A50 |
| -- | 65.0 | °C | ISO 306/B50 |
| Ball Pressure Test | Pass | IEC 335 | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 185 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trithene® TS 7003 | Petroquimica Triunfo | LDPE | Trithene® |
| Fiberfil® PP-60/VO/NH | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| FHR Polypropylene P4C6Z-022 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Elastollan® 1180A50 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| EPLAMID 6 GFR 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |