CELLwood® Pellets
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Microcell Composite Company |
| Trademark: | CELLwood® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nLDBGk_CELLwood-Pellets.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CELLwood foaming pellet is a compounded copolymer, which can be processing easily on most extrusion machines. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.600 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.70 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 1200 | MPa | |
| Break | 18.1 | MPa | |
| -- | 18.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 1.6 | % | |
| Break | 1.6 | % | |
| Flexural Modulus 3 | 1450 | MPa | ASTM D790 |
| Flexural Strength 4 | 30.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 7.9 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 91.9 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 CAM Tube | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Melos™ FM 1239 | Melos GmbH | TPO (POE) | Melos™ |
| Akulon® K125/A | DSM Engineering Plastics | Nylon 6 | Akulon® |
| BESTNYL SE00VI02AM | Triesa Plastics | Nylon 66 | BESTNYL |
| Hostacom T20C557 3211 | LyondellBasell Industries | PP Copolymer | Hostacom |