Trexprene® A64CI
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nKbwrM_Trexprene-A64CI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A64CI is a pre-colored, heat and UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This compound is primarily intended for interior automotive applications and can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.870 to 0.950 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 60 to 68 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Across Flow : 100% Strain | 2.30 | MPa | |
| Flow : 100% Strain | 3.90 | MPa | |
| Tensile Stress 2 | ISO 37 | ||
| Across Flow : Break | 5.70 | MPa | |
| Flow : Break | 4.50 | MPa | |
| Tensile Elongation 3 | ISO 37 | ||
| Across Flow : Break | 720 | % | |
| Flow : Break | 250 | % | |
| Tear Strength 4 | ISO 34-1 | ||
| Across Flow | 27 | kN/m | |
| Flow | 24 | kN/m | |
| Compression Set | |||
| 70°C, 24 hr | 31 | % | ASTM D395B |
| 70°C, 24 hr 5 | 31 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 1000 hr) | -2.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (110°C, 1000 hr) | -7.0 | % | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 20 | mm/min | ISO 3795 |
| Fogging - Dry Fog | 87 | % | SAE J1756 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Color Fastness - to Light 6 | Delta E < 3 | ||
| Odor Rating 7 | > 7.00 | ||
| Ozone Resistance (40°C) 8 | 0 Rating | ISO 1431-1 | |
| Weatherability | |||
| Arizona 9 | Delta E < 3 | ||
| Florida 10 | Delta E < 3 | SAE J1976 |
| Note Message | |
|---|---|
| 1 . | Type 1, 500 mm/min |
| 2 . | Type 1, 500 mm/min |
| 3 . | Type 1, 500 mm/min |
| 4 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 5 . | Type A |
| 6 . | SAE J2412, ISO 105-B06, Cond. 5, 1,240.8 kJ/m² |
| 7 . | GMW3205 Code B |
| 8 . | 100 pphm, Method A |
| 9 . | 105,000 TNR Langleys exposure per GMW3417 L1, F2, G1, T5 |
| 10 . | 2 years exposure, Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3035EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| GERMAFORM 9 GF 25 | Kunststoff-Kontor-Hamburg GmbH | Acetal (POM) Copolymer | GERMAFORM |
| HiFill® TPU/I GF25 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| LUVOCOM® 1100-8301 | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| OmniPro™ TPO MF20 HF HSV | OMNI Plastics, LLC | TPO | OmniPro™ |