SABIC® HDPE F4520
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGsWzr_SABIC-HDPE-F4520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B4520 is typically used for blow moulding packaging up to 20 l, combining medium stiffness with a good ESCR. This grade is typically used for packaging of aggressive detergents and technical articles such as spare fuel tanks, air- and cable ducts. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.16 | g/10 min | |
| 190°C/21.6 kg | 20 | g/10 min | |
| 190°C/5.0 kg | 0.89 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 150 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 800 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 22.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 31.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 850 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 22.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 23.0 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 181 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 5.0 | kJ/m² | |
| 23°C, Compression Molded | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 73.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature (DSC) | 130 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5755 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| TOTAL Polypropylene Aceso® Lumicene® MR 10MM0 S01 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Cellophane™ 335MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Sylvin 8225-90FU Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DF0029ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |