RTP 900 MG 10
| Category: | PSU , Polysulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGeUeI_RTP-900-MG-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Milled Glass |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Compressive Strength | 100 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 182 | °C | |
| 1.8 MPa, Unannealed | 177 | °C | |
| CLTE - Flow | 3.8E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity 1 | 0.27 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 2(in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 | |
| Arc Resistance | 100 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 332 to 371 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Injection Pressure | 68.9 to 124 | MPa |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 93036 B | RTP Company | Nylon 6 | RTP |
| SAXAMID™ 126F6RY01 | SAX Polymers | Nylon 6 | SAXAMID™ |
| ENFLEX S3170A HF | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Lucent PA G66-33 | Lucent Polymers, Inc. | Nylon 66 | Lucent PA |
| POLLITE 1001 | POLYROCKS CHEMICAL CO., LTD | PC | POLLITE |