FRIANYL® XT4 GF30 VOI
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGbpmb_FRIANYLXT4GF30VOI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PPA FLAME RETARDANT COMPOUND
PPA, 30% GLASS FIBER REINFORCED, FLAME RETARDANT V0, PBB AND PBDE FREE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.90 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 3.0 | -- | % | ISO 62 |
| Saturated, 23°C | 0.30 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 150 | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.2 | 2.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.5 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 42 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 45 | 48 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.5 | 7.5 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 280 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | 1.0E+11 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | V-0 | -- | UL 94 | |
| 0.8 mm | V-0 | -- | UL 94 | |
| 1.6 mm | V-0 | -- | UL 94 | |
| 3.2 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.8 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.8 mm | 800 | -- | °C | IEC 60695-2-13 |
| 3.2 mm | 875 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 20000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicostirolo 684V0 | Ravago Group | PS (HIPS) | Sicostirolo |
| Synres-Almoco EP 3505 | Synres-Almoco BV | Epoxy | Synres-Almoco |
| Aarolene® AVPS GP 100-1 | Aaron Industries Corp. | PS (GPPS) | Aarolene® |
| Bergamid™ A70 GK30 black 13539126 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ESENTTIA 03H82NA-TAR | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |