Sumikon® PM-6545
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGRqzK_SumikonPM6545.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-6545 type black is Glass fiber filled resol resin molding compound with good mechanical property and heat resistance. This grade suits UL1004. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.99 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.19 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.11 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 94.0 | MPa | JIS K6911 |
| Flexural Modulus | 20900 | MPa | JIS K6911 |
| Flexural Strength | 176 | MPa | JIS K6911 |
| Compressive Strength | 145 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.8 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 12 | kV/mm | JIS K6911 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 7.0E+12 | ohms | JIS K6911 |
| -- 3 | 8.0E+11 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA E450 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| TABOREN PH 79 T 20 | SILON s.ro | PP Homopolymer | TABOREN |
| Dugdale PVC Flexible Injection Molding - Shore A 58 Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| ICORENE® N1017 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| Hostacom TYC 2101N C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |