Haysite BMC 18600
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Haysite Reinforced Plastics |
| Trademark: | Haysite BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nGGvOZ_Haysite-BMC-18600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Haysite BMC 18600 is a Thermoset Polyester product filled with 15% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Molding Shrinkage - Flow | 0.22 | % | |
| Water Absorption (Equilibrium) | 0.11 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 43.4 | MPa | ASTM D638 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Compressive Strength | 103 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 210 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1(Oil) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 0.0850 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.067 | ASTM D150 | |
| Arc Resistance | 188 | sec | ASTM D495 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Temperature Rating | 180 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 14N5006 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Verolloy B5523 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| DOWLEX™ 2740G (Blown Film) | The Dow Chemical Company | LLDPE | DOWLEX™ |
| ECOVYLOPET® EMC2330 | TOYOBO America, Inc. | PET | ECOVYLOPET® |
| Karina WHITE PVC COMPOUND 801-10/94-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |