VICTREX® PEEK 150FW30

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nGGLqO_VICTREX-PEEK-150FW30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 30% reinforced with carbon fibre / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black.

Tribological applications with thin cross sections or long flow lengths for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Filler / Reinforcement	Carbon \PTFE, 30% filler by weight
Features	Semicrystallization Low friction coefficient High strength Good liquidity Good chemical resistance Good wear resistance Compliance of Food Exposure
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Black
Forms	Particles
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.43	g/cm³	ISO 1183
Spiral Flow	16.5	cm	Internal method
Molding Shrinkage ²			ISO 294-4
Vertical flow direction : 180°C	0.60	%	ISO 294-4
Flow direction : 180°C	0.10	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.040	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.30	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	85		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	15000	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	180	MPa	ISO 527-2
Fracture, 125°C	115	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	1.8	%	ISO 527-2
Flexural Modulus (23°C)	14500	MPa	ISO 178
Flexural Stress			ISO 178
23°C	270	MPa	ISO 178
125°C	170	MPa	ISO 178
175°C	100	MPa	ISO 178
225°C	60.0	MPa	ISO 178
Compressive Stress			ISO 604
23°C	210	MPa	ISO 604
120°C	155	MPa	ISO 604
200°C	60.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	35	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	5.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	35	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	325	°C	ISO 75-2/Af
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : > 143°C	9.0E-5	cm/cm/°C	ISO 11359-2
Flow : < 143°C	9.0E-5	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	4.5E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	1.1E-4	cm/cm/°C	ISO 11359-2
Specific Heat Capacity	1.80	J/kg/°C	DSC

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ³(23°C)	1.0E+7	ohms·cm	IEC 60093

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	260	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	365	°C
Middle Temperature	370 - 375	°C
Front Temperature	380	°C
Nozzle Temperature	385	°C
Mold Temperature	170 - 200	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	385°C nozzle
3 .	1V

Resin Grade	Manufacturer	Category	Trademark
MARPOL® COPP 0.5.NB	Marco Polo International, Inc.	PP Impact Copolymer	MARPOL® COPP
TEKAMID™ H14ST	Mando Advanced Materials Co., Ltd.	ABS+Nylon	TEKAMID™
HiFill® PA6 G/M40 L UV	Techmer Engineered Solutions	Nylon 6	HiFill®
Huafon JF-P-6760 / JF-I-6722	Huafon Group Co., Ltd.	PUR-Ester	Huafon
SABIC® PC PC0703R resin	SABIC Innovative Plastics Asia Pacific	PC	SABIC® PC