EL-Lene™ H1000PC
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nFgbFd_EL-Lene-H1000PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H1000PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. EL-Lene H1000PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.25 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | > 10000 | hr | ASTM D1693 |
| Carbon Black Content | 2.3 | % | ISO 6964 |
| Carbon Black Dispersion | < 3 | ISO 18553 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Slow Crack Growth (80°C) | > 500 | hr | ISO 13479 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 60 | min | EN 728 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rapid Crack Propagation | > 1.00 | MPa | ISO 13477 |
| Resistance to Gas Components | > 20.0 | hr | ISO 1167 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/100 | ||
| Yield | 23.0 | MPa | |
| Break | > 30.0 | MPa | |
| Tensile Strain (Break) | > 600 | % | ISO 527-2/100 |
| Flexural Modulus | 1000 | MPa | ASTM D790 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Melt Temperature | 200 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE OM-1135N | Teknor Apex Company | TPE | Sarlink® TPE |
| SUMILITE® PVC VSS-ET110 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| Delrin® 127UV BK701 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Iupilon® RS-1001R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| SABIC® PC PC5800 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |