Trilene® HE2.0TF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Trilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nFOeQR_Trilene-HE2-0TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trilene HE2.0TF is a polypropylene homopolymer for sheet extrusion and thermoforming (SPPF) applications. This grade uses Unipol® polypropylene technology, with latest catalyst technology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.4 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 14 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1290 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 3 |
| Peak Melting Temperature 4 | 161 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 240 | °C | |
| Take-Off Roll | 25.0 - 40.0 | °C |
| Extrusion instructions |
|---|
| Sheet Temperature, forming zone: 157 to 160°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 标准 B (120°C/h) |
| 4 . | 10°C/min, 2nd heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/TP-GP2 | Polymer Resources Ltd. | PC+Polyester | PRL |
| Stanyl® TW250F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| TAIRIPRO K3004 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| VECTRA® FIT70 | Celanese Corporation | LCP | VECTRA® |
| CERTENE™ PRM-35 | Muehlstein | PP Random Copolymer | CERTENE™ |