Andur M-11 (94% 1,4BD, 6% TMP)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nFF8gd_Andur-M-11-94-1-4BD-6-TMP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur M-11 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 92 | ASTM D2240 | |
| Shaw D | 42 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 2% strain | 0.689 | MPa | ASTM D695 |
| 5% strain | 1.72 | MPa | ASTM D695 |
| 10% strain | 3.45 | MPa | ASTM D695 |
| 15% strain | 4.83 | MPa | ASTM D695 |
| 20% strain | 6.21 | MPa | ASTM D695 |
| 25% strain | 7.93 | MPa | ASTM D695 |
| 50% strain | 29.0 | MPa | ASTM D695 |
| Taber Abrasion Resistance | 50.3 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 7.93 | MPa | ASTM D412 |
| 200% strain | 17.2 | MPa | ASTM D412 |
| 300% strain | 27.6 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 42.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 410 | % | ASTM D412 |
| Compression Set | 30 | % | ASTM D395 |
| Bayshore Resilience | 28 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 - 8.0 | min | |
| Demold Time | 35 | min |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 660 pliAverage Split Tear, ASTM D1938: 235 pliStoichiometry Curative Level: 95%NBS Abrasion: 220% Rubber StandardParts of curative per 100 parts Andur M-11, 8.9% NCO: 9.08 parts by weightParts of curative per 100 parts Andur M-11, 9% NCO: 9.18 parts by weightParts of curative per 100 parts Andur M-11, 9.1% NCO: 9.28 parts by weightParts of curative per 100 parts Andur M-11, 9.2% NCO: 9.39 parts by weightMix Temperature: Andur M-11: 176-194°F Curative 1,4BD/TMP: 77-158°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 90.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® TM30CW | BASF Leuna GmbH | Nylon 66/6 | Miramid® |
| SCHULADUR® A GF 20 | A. Schulman Europe | PBT | SCHULADUR® |
| AKROMID® B3 GF 25 1 L black (4637) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Elastron® G P.G401.A50.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Dow Corning® MG-2401 | Dow Corning Corporation | Silicone | Dow Corning® |