TAISOX 2214
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nCCKtT_TAISOX-2214.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 2214 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 2214 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 186 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 235 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 10.3 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 41.2 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 33.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 760 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 260 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 360 | g | ASTM D1922 |
| TD : 38 µm, blown film | 820 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 51 | ASTM D2457 | |
| Clarity | 60.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PP PRM5203 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Novamid® 2020J | DSM Engineering Plastics | Nylon 66/6 | Novamid® |
| ESTAPROP 1040 V2 HK BLU 6237 PANT 285C | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Kepamid® 2320CF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ THERMOCOMP™ UF006H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |