SABIC® HDPE ICP4907S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nBLIeZ_SABIC-HDPE-ICP4907S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE ICP4907S is part of SABIC's high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP4907S is typically used for state of the art blow moulding UN certified Intermediate Bulk Containers and Heating Oil Tanks, up to 1000 liters and more. This UV-stabilised and food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 800 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 950 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 23.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 34.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 24.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 30.0 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 192 | J/g | ISO 11357-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (-30°C, Compression Molded) | 17 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 77.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-17H | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Bergamid™ A70 GK30 black 13539126 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Caltex PP HR13G | GS Caltex | PP, Unspecified | Caltex PP |
| AXELERON™ GP 7590 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| ExxonMobil™ LDPE LD 650 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |