Andur M-33 (DEG)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nBKrg0_Andur-M-33-DEG-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur M-33 is a low melting MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in low temperature applications. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 2% strain | 0.241 | MPa | ASTM D695 |
| 5% strain | 0.655 | MPa | ASTM D695 |
| 10% strain | 1.38 | MPa | ASTM D695 |
| 15% strain | 2.14 | MPa | ASTM D695 |
| 20% strain | 2.90 | MPa | ASTM D695 |
| 25% strain | 3.72 | MPa | ASTM D695 |
| 50% strain | 10.1 | MPa | ASTM D695 |
| Taber Abrasion Resistance | 10.5 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.65 | MPa | ASTM D412 |
| 300% strain | 9.38 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 46.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Compression Set | 45 | % | ASTM D395 |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 11 - 13 | min | |
| Demold Time | 75 | min |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 410 pliAverage Split Tear, ASTM D1938: 50 pliStoichiometry Curative Level: 97%NBS Abrasion: 185% Rubber StandardParts of curative per 100 parts Andur M-33, 6.75% NCO: 8.11 parts by weightParts of curative per 100 parts Andur M-33, 6.8% NCO: 8.17 parts by weightParts of curative per 100 parts Andur M-33, 6.85% NCO: 8.23 parts by weightParts of curative per 100 parts Andur M-33, 6.9% NCO: 8.29 parts by weightParts of curative per 100 parts Andur M-33, 6.95% NCO: 8.35 parts by weightParts of curative per 100 parts Andur M-33, 7% NCO: 8.41 parts by weightMix Temperature: Andur M-33: 176-194°F Curative DEG: 77-158°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 80.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROBLEND 66 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| Niche PCM12BK | Niche Polymer, LLC | PC | Niche |
| Network Polymers PP PPH 30 2000 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Jackdaw PC DS10PR6656 | Jackdaw Polymers | PC | Jackdaw PC |
| PLEXIGLAS® Sheet Soundstop XT BirdGuard | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |