Bayblend® 2953
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n9Zrwr_Bayblend-2953.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; Vicat/B 120 temperature = 113°C; for electroplating applications. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 44.0 | MPa | |
| Break, 23°C | 47.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 3.6 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 2(3.5% Strain, 23°C) | 65.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 3(23°C) | 5.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 46 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/B50 |
| -- | 113 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNIPA® im | Nytef Plastics, Ltd. | Nylon 66 | UNIPA® |
| Di-Pak™ E-4888 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| KOCETAL® WR303 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| NHU-PPS 21150C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |
| LEXAN™ HPX4 resin | SABIC Innovative Plastics | PC | LEXAN™ |