RTP 3400 M-340
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n8GyG2_RTP-3400-M-340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 246 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 332 to 354 | °C | |
| Middle Temperature | 332 to 354 | °C | |
| Front Temperature | 332 to 354 | °C | |
| Nozzle Temperature | 343 to 379 | °C | |
| Mold Temperature | 65.6 to 121 | °C | |
| Injection Pressure | 103 to 138 | MPa | |
| Clamp Tonnage | 5.5 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 223 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| TOPAS® 8007S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| CP PRYME® Polypropylene PPH100-20M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| Kepamid® 2340GM7 | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| LNP™ STAT-KON™ OE004A compound | SABIC Innovative Plastics Europe | PPS, Branched | LNP™ STAT-KON™ |