Retpol® C3 200 TF HS
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n7rCUV_Retpol-C3-200-TF-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Propak C3 200 TF HS is a 20% talc filled copolymer polypropylene compound. It is a low to medium flow injection moulding grade developed for rigid components and is manufactured in accordance with Australian Standard AS 2070, "Plastic Materials for Food Contact Use". The ingredients used in this formulation are referenced in the US Code of Federal Regulations, Volume 21. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.0 to 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 86 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 73 | ||
| Shore D, 15 sec, 3.00 mm | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 55 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 900 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 60.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polypropylene C7038-38NA | Trinseo | PP Impact Copolymer | Polypropylene |
| Taitacell EPS-301ML | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Cri-Line LC-915-BR | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Karina BLACK PVC COMPOUND 850-48/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Politer 20 GB | Poliblend S.p.a. | PBT | Politer |