EPO-TEK® OE184
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n6tCMU_EPO-TEK-OE184.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, high Tg, optically clear epoxy for packaging and assembly of fiber optics cables and components. It is suggested for termination of fibers into ferrules, or fabrication of waveguide devices. It is a faster curing alternative to EPO-TEK® 353ND. Complies with USP Class VI biocompatibility standards. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 100 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.6E-5 | cm/cm/°C | |
| -- 3 | 1.7E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.570 | ||
| Transmittance | |||
| 700 to 1400 nm | > 95.0 | % | |
| 1550 nm | 95.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 474 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus (23°C) | 1.60 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.070 | % | |
| 250°C | 0.14 | % | |
| 300°C | 0.39 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 3.0 to 4.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | < 60 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 | ||
| Lap Shear Strength (23°C) | 11.3 | MPa | |
| Relative Permittivity (1 kHz) | 3.45 | ||
| Volume Resistivity (23°C) | > 7.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 7.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P254-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| StarMediflex P 7080-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| ALFATER XL® A70I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| ASTAMID™ MA3WG63 | Marplex Australia Pty. Ltd. | Nylon 66 | ASTAMID™ |
| Dugdale PVC Rigid Extrusion White Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |