Amilan® CM1011G-45
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n6epyP_Amilan-CM1011G-45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM1011G-45 is a Polyamide 6 (Nylon 6) product filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.40 to 0.60 | -- | % | |
| Flow : 3.00 mm 2 | 0.10 to 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | |
| Saturation, 23°C | 5.3 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 95 | -- | ||
| R-Scale, 23°C | 121 | -- | ||
| R-Scale, 80°C | 30 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 290 | 250 | MPa | |
| 23°C | 205 | 130 | MPa | |
| 80°C | 120 | 85.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 3.0 | 3.0 | % | |
| Break, 23°C | 3.0 | 3.0 | % | |
| Break, 80°C | 5.0 | 5.0 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 16100 | 14300 | MPa | |
| 23°C | 13800 | 8100 | MPa | |
| 80°C | 7100 | 5000 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 385 | 325 | MPa | |
| 23°C | 340 | 210 | MPa | |
| 80°C | 185 | 125 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 260 | 220 | MPa | |
| 23°C | 190 | 120 | MPa | |
| 80°C | 100 | 70.0 | MPa | |
| Shear Strength (23°C) | 95.0 | 75.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.350 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 15 | 17 | kJ/m² | |
| 23°C | 19 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 90 | 95 | kJ/m² | |
| 23°C | 100 | 120 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | -- | J/kg/°C | |
| Thermal Conductivity | 0.40 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | 15 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 5.00 | 9.50 | ||
| 23°C, 1 kHz | 4.90 | 7.40 | ||
| 23°C, 1 MHz | 4.20 | 4.50 | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.030 | 0.16 | ||
| 23°C, 1 kHz | 0.030 | 0.15 | ||
| 23°C, 1 MHz | 0.030 | 0.060 | ||
| Arc Resistance 6 | 104 | 109 | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 5433 | Colorite Polymers | PVC, Unspecified | Unichem |
| Hyundai EP PPF HT340J | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| PONACOM PE 4428 | Ponachem Compound GmbH | HDPE | PONACOM PE |
| Sylvin 8687-55 Green 3159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BKV 30 DUS000 000000 | LANXESS GmbH | Nylon 6 | Durethan® |