HIFOR® LT74147
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n62xLH_HIFOR-LT74147.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WESTLAKE HIFOR Polyethylene LT74147 is a high strength linear low density polyethylene containing medium slip and high antiblock. It is designed for blown applications and is well suited for consumer and industrial packaging markets which require impact and tear strength. Films produced usign LT74147 exhibit low imperfections and facilitate production at thinner guages. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 221 | MPa | |
| 1% Secant, TD | 241 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 50.3 | MPa | |
| TD : Break | 39.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 750 | % | |
| TD : Break | 1000 | % | |
| Dart Drop Impact | 170 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 | |
| Haze | 35 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP640J | LyondellBasell Industries | PP Homopolymer | Moplen |
| Ultramid® B36 LN | BASF Corporation | Nylon 6 | Ultramid® |
| ESTABLEND PC ABS 4502 V0 | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Hyundai EP PPF HT940 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Plaslube® PA6/6 GF40 ML2 HS | Techmer Engineered Solutions | Nylon 66 | Plaslube® |