Radilon® A USX016W 333 NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n5uXc5_Radilon-A-USX016W-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 injection moulding grade. Toughened, heat stabilized. Black colour. Suitable for parts requiring excellent impact resistance and high flexibility. Very good properties retention after ageing. ISO 1043 : PA66-HI |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 2.0 | -- | % | |
| Flow | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1950 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 50.0 | -- | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 20 | -- | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 60 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 2 | 1800 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 70.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Melting Temperature 4 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 290°C Melt Temp / 70°C Mold Temp / 30 Mpa Cavity press |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RALUPOL® UP 4566 | RASCHIG GmbH | Polyester, TS | RALUPOL® |
| Tisester® PBT 30 GFR FR | Tisan | PBT | Tisester® |
| Wellamid® GF1398 BK12 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Hyundai EP Adhesives VE400S/1002 | HYUNDAI EP Co., Ltd. | EVA | Hyundai EP Adhesives |
| LUVOCOM® 3-8896/WT/V-0 | LEHVOSS Group | Nylon 6 | LUVOCOM® |