RIALFLAME B V0H 15 H 20 T
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFLAME |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n3utAw_RIALFLAME-B-V0H-15-H-20-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene self-extinguishing compound, classifiable according to the norms of UL-94, file E178416, V-0 up to 1.5mm. halogen content, free from PBDE and PBB, conforms to RoHS. Specific thermal stabilization ofr use at high application temperature. High flowability, excellent dimensional stability, good compromise between stiffness and impact strength, specifc grade for injection molding, available in natural and colored as per sample. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 1.0 | % | |
| Ash Content | 20 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 20.8 | day | ISO 4577 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Test | Pass | IEC 60695-2-12 | |
| Needle Flame Test 1(2.00 mm) | Pass | IEC 60695-2-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 22.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 10 | % | |
| Flexural Modulus 2(23°C) | 2800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.5 | kJ/m² | |
| 23°C | 2.9 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm 3 | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Ignition Temperature | 725 | °C | IEC 60695-2-13 |
| Oxygen Index 4 | 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A-B |
| 2 . | 2.0 mm/min |
| 3 . | up to 1.5mm |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® P 70 PS | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Hostaform® C 2521 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Hyundai EP Matt MF401/Natural | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Matt |
| Ixef® 1027 | Solvay Specialty Polymers | PARA | Ixef® |
| Iupilon® EGN2010KR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |