OP - PC - Filled 30GF
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Filled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n3cil4_OP---PC---Filled-30GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OP - PC - Filled 30GF is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8620 | MPa | ASTM D638 |
| Tensile Strength (Break) | 131 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Compressive Strength | 124 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 288 to 293 | °C | |
| Middle Temperature | 299 to 316 | °C | |
| Front Temperature | 299 to 316 | °C | |
| Nozzle Temperature | 299 to 316 | °C | |
| Processing (Melt) Temp | 293 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Injection Pressure | 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| alphalon™ 27 C | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Daelim Po1y® PP-246H | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Fainplast PVC PH 83 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| ICORENE® 8040 WS | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| Sylvin 8200-90 Clear 8464 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |