AKROLOY® PA GF 60 8 black (4174)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n38vqq_AKROLOY-PA-GF-60-8-black-4174-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 60 8 black (4174) is a 60% glass fibre reinforced polyamide blend with very high stiffness and strength, as well as reduced moisture absorption, modified for the respective application. Applications are components with tight dimensional tolerances even under high mechanical load, especially in drinking water industry. It is a very cost effective alternative for zinc- and aluminium diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.72 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 6.00 | -- | cm³/10min | ISO 1133 |
| Humidity Absorption - 62% RH (70°C) | 1.1 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 60 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 22000 | 20000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 275 | 210 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 23000 | 21200 | MPa | ISO 178 |
| Flexural Stress 2 | 435 | 370 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | -- | kJ/m² | |
| 23°C | 18 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 90 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 200 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 255 | -- | °C | DIN EN 11357-1 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 1920 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| YUCLAIR® CA100 | SK Global Chemical | LLDPE | YUCLAIR® |
| Chemical Resources LLD100929 | Chemical Resources, Inc. | LLDPE | Chemical Resources |
| LNP™ STAT-LOY™ M3000C compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-LOY™ |
| Rotuba CAB B900 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |