LNP™ STAT-KON™ 9X08403C compound
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n3103i_LNP-STAT-KON-9X08403C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON 9X08403C is a compound based on Liquid Crystal Polymer (LCP) resin containing Carbon Fiber. Added features of this material are: Clean Compounding System, High Temperature, Flame Retardant, Electrically Conductive, Good barrier against water and oxygen. Also known as: LNP* STAT-KON* Compound 9X08403C Product reorder name: 9X08403C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.20 | % | |
| Across Flow | 0.52 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 14800 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 153 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 2.7 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 14400 | MPa | ASTM D790 |
| Flexural Strength | 53.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 830 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 280 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+9 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+5 to 1.0E+9 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 1.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 327 to 360 | °C | |
| Middle Temperature | 328 to 360 | °C | |
| Front Temperature | 329 to 360 | °C | |
| Nozzle Temperature | 330 to 360 | °C | |
| Processing (Melt) Temp | 331 to 360 | °C | |
| Mold Temperature | 66.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SI302G30 | RJM International, Inc. | PET | RJM |
| ESTAPROP KUR 1520 TG05 | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| ExxonMobil™ LLDPE LL 1002 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Sylvin 8250-70 Brown 7461 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ IFL21 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |