VITAMIDE® BR3XNT6509
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n2Sxqf_VITAMIDE-BR3XNT6509.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BR3XNT6509 is a Polyamide 6 (Nylon 6) product filled with 50% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 235 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7700 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 220 | MPa | ISO 178 |
| Break | 220 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 60 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Faraprene 200 | Primex Plastics Corporation | TPE Alloy | Prime Faraprene |
| Moplen EP318R | PolyMirae | PP Copolymer | Moplen |
| ARC ARC10H | ARC Resin Corporation | Acetal (POM) Homopolymer | ARC |
| APEX® 94-A0055A-80 | Teknor Apex Company | PVC, Flexible | APEX® |
| SECCO LL0220AA | Shanghai SECCO Petrochemical Co., Ltd | LLDPE | SECCO |