UNIVAL™ DMDG-6200 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n2NHH7_UNIVAL-DMDG-6200-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
UNIVAL™DMDG-6200 NT 7 is a multi-purpose polymer, a high-speed production line using blow molded containers, which are used to package household chemicals, toilet products, cosmetics, health and medical aids, food, etc. This product is specially developed to achieve excellent processing performance on all blow molding equipment, including continuous extruder equipment.
U.S. FDA-DMF Meet the requirements of the Canadian Health Products and Food Agency (HPFB): No objection (with restrictions) EU, No 10/2011 Please check the regulations for complete details. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.953 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.38 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 41 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 40.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 24.8 | MPa | ASTM D638 |
| Fracture | 23.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 570 | % | ASTM D638 |
| Flexural Modulus | ASTM D790B | ||
| 2% secant | 814 | MPa | ASTM D790B |
| Tangent | 1310 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 118 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HH 1600 | Plastic Solutions, Inc. | PS (Specialty) | PrimaFlex® |
| Santoprene™ 8211-45 | ExxonMobil Chemical | TPV | Santoprene™ |
| Torlon® 5030 | Solvay Specialty Polymers | PAI | Torlon® |
| Hostalen PP H2222 36 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| LUVOCOM® 1105-7285/EM/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |