Rilsan® BMN G8 TLDA
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n182A6_Rilsan-BMN-G8-TLDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BMN G8 TLDA is a polyamide 11 produced from a renewable source. This grade is designed for injection molding with improved friction properties and is approved for drinking water contact: WRAS (UK). MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 0.80 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 75 | ||
| Shore D, 15 sec | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 40.0 | MPa | |
| Break | 52.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, MHLRS, 12-010 CD | ISO 1874 | |
| Renewable Carbon Conent | > 94 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 210 to 280 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 L | RTP Company | PESU | RTP |
| Sindustris POM FW701S | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| EXCELLOY AK15 | Techno Polymer Co, Ltd. | ABS+Nylon | EXCELLOY |
| LNP™ THERMOCOMP™ DC006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| Petrotene® PP T3 CINZA 7743 SB28 PH341 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |