PENTAMID A GV50 H RC black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mziOqf_PENTAMIDAGV50HRCblack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, 50% glass fiber reinforced, ReCompound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.45 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | ISO 62 |
| Viscosity Number | 132 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14500 | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus | 13300 | -- | MPa | ISO 178 |
| Flexural Stress | 330 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.80 | -- | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.2 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA66, MHRC, 14-150 N, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.030 - 0.11 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 285 - 310 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 80.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VS430 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| 3M™ Dyneon™ PTFE Compound TF 4216 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| INELEC ABSASFR | Infinity LTL Engineered Compounds | ABS | INELEC |
| LNP™ THERMOCOMP™ UF007SXC compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |
| POCAN® B 600 000000 | LANXESS GmbH | PBT | POCAN® |