Teflon® PTFE 613A X

Category:	PTFE , Polytetrafluoroethylene
Manufacturer:	DuPont Fluoropolymers
Trademark:	Teflon® PTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mzV5rB_Teflon-PTFE-613A-X.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DuPont™ Teflon® PTFE 613A X is a polytetrafluoroethylene fine powder resin used primarily for paste extrusion. Teflon® PTFE 613A X offers the excellent combination of properties typical of the Teflon® fluoroplastic resins: chemical inertness to nearly all industrial chemicals and solvents superior in-use thermal stability (low thermal instability index) exceptional dielectric properties, stable with frequency and temperature toughness and flexibility low coefficient of friction non-stick characteristics negligible moisture absorption excellent weather resistance service temperature up to 260°C (500°F) useful properties at -240°C (-400°F) moderate stiffness and high ultimate elongation Teflon® PTFE 613A X is designed for processing at low to medium reduction ratios of 10:1 to 300:1. It is designed to facilitate the production of high-quality, low-density tape and beading. Teflon® PTFE 613A X meets the requirements of ASTM D 4895-10, Type I, Grade 1, Class B.

Message

DuPont™ Teflon® PTFE 613A X is a polytetrafluoroethylene fine powder resin used primarily for paste extrusion. Teflon® PTFE 613A X offers the excellent combination of properties typical of the Teflon® fluoroplastic resins:

chemical inertness to nearly all industrial chemicals and solvents

superior in-use thermal stability (low thermal instability index)

exceptional dielectric properties, stable with frequency and temperature

toughness and flexibility

low coefficient of friction

non-stick characteristics

negligible moisture absorption

excellent weather resistance

service temperature up to 260°C (500°F)

useful properties at -240°C (-400°F)

moderate stiffness and high ultimate elongation

Teflon® PTFE 613A X is designed for processing at low to medium reduction ratios of 10:1 to 300:1. It is designed to facilitate the production of high-quality, low-density tape and beading. Teflon® PTFE 613A X meets the requirements of ASTM D 4895-10, Type I, Grade 1, Class B.

General Information
Features	Good Chemical Resistance Good Electrical Properties Good Thermal Stability Good Toughness Good Weather Resistance High Elongation Low Friction Low Temperature Resistant Solvent Resistant
Uses	Insulation Wire & Cable Applications
Forms	Powder
Processing Method	Extrusion Ram Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.14	g/cm³	ASTM D4895, ISO 12086
Apparent Density	0.44	g/cm³	ASTM D4895, ISO 12086
Average Particle Size
--	500	µm	ISO 12086
--	500	µm	ASTM D4895

Thermal	Nominal Value	Test Method
Thermal Instability Index
--	< 50.0	ASTM D4895
--	< 50.0	ISO 12086

Additional Information	Nominal Value	Unit	Test Method
Rheometer Pressure - Reduction Ratio 100:1
--	27.6	MPa	ISO 12086
--	27.6	MPa	ASTM D4895

Thermal	Nominal Value	Unit	Test Method
Melting Temperature
-- ¹	327	°C	ISO 12086, ASTM D4895
-- ²	342	°C	ASTM D4895, ISO 12086

Note Message
1 .	Second
2 .	Initial

Resin Grade	Manufacturer	Category	Trademark
MBA PS 3122 UV 70/15	MBA Polymers	PS (GPPS)	MBA PS
Ravamid® B T NC	Ravago Group	Nylon 6	Ravamid®
Verolloy B5524	PlastxWorld Inc.	ABS+PBT	Verolloy
WELLAMID Nylon 6000/42 CP	CP-Polymer-Technik GmbH & Co. KG	Nylon 6	WELLAMID Nylon
YUNGSOX® PP 3015	Formosa Polypropylene	PP Impact Copolymer	YUNGSOX® PP