Moplen EPQ30R
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Shazand (Arak) Petrochemical Corporation |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mz4II7_Moplen-EPQ30R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EPQ30R is a high molecular weight, hetrophasic polypropylene copolymer designed for extrusion applications which require a balance of high stiffness and very high impact strength. Moplen EPQ30R offers excellent process ability in extrusion. The final items show very good mechanical properties, even at temperatures down to -20C. Major applications of Moplen EPQ30R are profiles, pipes, ducts for electrical distribution and automotive parts. This grade is also used for extrusion blow moulding pigmented, glossy monolayer bottles for toiletries, detergents and foodstuffs. Moplen EPQ30R is also well suited for corrugated board and sheet for thermoforming. * Moplen EPQ30R is suitable for food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 76 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 14 | % | ASTM D638 |
| Flexural Modulus | 1150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 60 | J/m | |
| 23°C | > 500 | J/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oven Aging (150°C) | 2.7 | month | ASTM D3012 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502 Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| RTP 800 GB 30 Z | RTP Company | Acetal (POM) Copolymer | RTP |
| Karina WHITE PVC COMPOUND 801-10/94-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PHOENIX™ 9653 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Plenco 00714 (Injection) | Plastics Engineering Co. | Mel Phenolic | Plenco |