Generic PPS, Linear - Carbon Fiber
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mxwmtu_Generic-PPS-Linear---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS, Linear - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.37 - 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.070 - 0.61 | % | ASTM D955 |
| Transverse flow : 23°C | 0.35 - 0.80 | % | ASTM D955 |
| 23°C | 0.070 - 0.39 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 - 0.051 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0E-3 - 0.031 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 10300 - 24200 | MPa | ASTM D638 |
| 23°C | 10300 - 30900 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 127 - 187 | MPa | ASTM D638 |
| Fracture, 23°C | 102 - 181 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 0.77 - 1.7 | % | ISO 527-2 |
| Fracture, 23°C | 1.2 - 1.6 | % | ASTM D638 |
| Fracture, 23°C | 0.99 - 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8450 - 21300 | MPa | ASTM D790 |
| 23°C | 9460 - 27700 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 193 - 283 | MPa | ASTM D790 |
| 23°C | 143 - 431 | MPa | ISO 178 |
| Coefficient of Friction | 0.14 - 0.47 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 14 - 25 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 36 - 75 | J/m | ASTM D256 |
| 23°C | 5.0 - 8.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 390 - 640 | J/m | ASTM D256 |
| 23°C | 24 - 35 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 4.90 - 16.7 | J | ASTM D3763 |
| 23°C | 1.36 - 3.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 108 - 267 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 220 - 270 | °C | ISO 75-2/A |
| Continuous Use Temperature | 219 - 220 | °C | ASTM D794 |
| CLTE - Flow | 8.4E-6 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.75 - 6.0 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0 - 6.3E+3 | ohms | ASTM D257 |
| -- | 2.0 - 2.5E+4 | ohms | IEC 60093 |
| Insulation Resistance (23°C) | 10 - 1.0E+6 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 136 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Middle Temperature | 320 - 327 | °C | |
| Front Temperature | 330 - 338 | °C | |
| Processing (Melt) Temp | 318 - 330 | °C | |
| Mold Temperature | 152 - 165 | °C | |
| Back Pressure | 0.258 - 0.264 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS, Linear - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Delrin® AF Blend | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| XYRON™ L524V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Desmopan® DP 85085A DPS 055 | Covestro - PUR | TPU, Unspecified | Desmopan® |
| GELOY™ XP4025 resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |
| Sinvicomp SSZ6309 KD11 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |