LOFEX® A321A
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mwNerh_LOFEX-A321A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A321A is Polyester film is optically clear and inside corona / outside acryl treated with enhanced adhesion to inks and coatings. So, it can use by tape, label, print film and semiconductor parts. Also, it has excellent properties by tensile strength, proper elongation and the thermal contraction rate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.30 | ||
| vs. Itself - Static | 0.35 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 100 µm | 196 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 100 µm | 170 | % | |
| TD : Break, 100 µm | 120 | % | |
| F5 | ASTM D882 | ||
| MD : 100.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| Surface Treatment | Inside (Corona)/Outside (Acryl) |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, 100 µm) | 160 | ASTM D523 | |
| Transmittance (100 µm) | 89.0 | % | ASTM D1003 |
| Haze (100 µm) | 1.3 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4955A | Teknor Apex Company | TPE | Telcar® |
| TUFNYL® SXXIC FA BEIGE | SRF Ltd. | Nylon 6 | TUFNYL® |
| NAXALOY® 773 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| Iupiace® AN80 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LNP™ LUBRICOMP™ WFP36 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |