Infino AE-2130
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mvI5GG_Infino-AE-2130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino AE-2130 is a Polycarbonate + PET (PC+PET) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/2.16 kg | 2.8 | g/10 min | |
| 260°C/5.0 kg | 21 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Ash Content | |||
| -- | 4.0 | % | ISO 3451 |
| -- | 4.0 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Break 3 | 56.0 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 90 | % | ASTM D638 |
| Break | 90 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| -- | 2500 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength 6 | |||
| -- | 81.0 | MPa | ASTM D790 |
| -- | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 33 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 550 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 180 | J/m | ASTM D256 |
| 23°C 8 | 38 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 128 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 120 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 98.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 132 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A3 GF30 | A. Schulman Inc. | PBT+ASA | SCHULADUR® |
| Sicoklar E81.22 | Ravago Group | PC | Sicoklar |
| NuSil MED-6655 | NuSil Technology | Silicone | NuSil |
| Hyrene® PSCRY 14 | Entec Polymers | PS (GPPS) | Hyrene® |
| SQUARE® LIM1550-35A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |