DENILUB Y 50G 0Mo
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENILUB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | muT9Ub_DENILUB-Y-50G-0Mo.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 50% glass fiber reinforced with molybdenum disulfide. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 240 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.40 | ||
| Static | 0.47 | ||
| Wear Factor 1 | 35.0 | 10^-10 m³ h/N·m·h |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 11 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 256 | °C | ASTM D648A |
| Vicat Softening Temperature | 254 | °C | ASTM D1525 2 |
| Note Message | |
|---|---|
| 1 . | Thrust Washer |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Fluorosint® 500 | Quadrant Engineering Plastic Products | PTFE | Quadrant EPP |
| SUPREME Specialty PS SP6630 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| NORYL™ 6390C resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| Edgetek™ NJ-30GF/000 Natural | PolyOne Corporation | Nylon 12 | Edgetek™ |
| Durethan® BKV 30 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |