NYLOY® PG-0030N
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | msofF2_NYLOY-PG-0030N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® PG-0030N is a Polypropylene material filled with 30% glass fiber. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.960 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.63 | % | |
| Across Flow | 1.0 | % | |
| Ash Content | 30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 97 | ASTM D785 | |
| R-Scale | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 74.5 | MPa | ASTM D638 |
| -- | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5250 | MPa | ASTM D790 |
| -- | 5450 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 106 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 74 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 158 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 147 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 144 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY A001 | Polyram Ram-On Industries | Nylon 66+PP | RAMLLOY |
| Next Nylon 66 Prime Series PG33-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Borcom™ WG140AI | Borealis AG | PP, Unspecified | Borcom™ |
| Devcon Metal Welder™ | Devcon | Epoxy | Devcon |
| Huafon JF-W-DP4050 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |