LNP™ STAT-KON™ SE003 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ms6zG7_LNPSTATKONSE003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON SE003 is a compound based on Nylon 12 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound SC-1003 Product reorder name: SE003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 | g/cm³ | ASTM D792 |
| -- | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.50 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.30 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- | 8700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 105 | MPa | ASTM D638 |
| Fracture | 105 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.8 | % | ASTM D638 |
| Fracture | 3.9 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 7000 | MPa | ISO 178 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 730 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 13.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 176 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 163 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 160 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 2.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 232 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 227 - 238 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC202E | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Ad-Tech Urethanes UC-4675 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| Cri-Line HFLT-820 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Sylvin 4299-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Adstif EA648P | LyondellBasell Industries | PP Impact Copolymer | Adstif |