LUVOCOM® NY-4/PL/15/BK Datasheet,Nylon 612,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®NY-4/PL/15/BK is a polyamide 612 (nylon 6/12) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of NY-4/PL/15/BK are: Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories Electrical/electronic applications textile/fiber Automotive Industry business/office supplies

General Information
Additive	PTFE lubricant
Features	Low friction coefficient Good wear resistance Lubrication
Uses	Gear Textile applications Engineering accessories Switch Application in Automobile Field Business equipment Bearing
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.11	g/cm³	ISO 1183
Molding Shrinkage	1.4 - 2.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.35	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	45.0	MPa	ISO 527-2
Tensile Strain (Yield)	4.0	%	ISO 527-2
Flexural Modulus	2000	MPa	ISO 178
Flexural Stress	70.0	MPa	ISO 178
Coefficient of Friction
Dynamic	0.27
Static	0.21
Flexural Strain at Flexural Strength	6.5	%	ISO 178

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	29	kJ/m²	ISO 179/1fU

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+12	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	220 - 260	°C
Middle Temperature	225 - 265	°C
Front Temperature	230 - 275	°C
Nozzle Temperature	230 - 285	°C
Processing (Melt) Temp	280	°C
Mold Temperature	60.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 612 , Polyamide 612
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mrdTPx_LUVOCOM-NY-4-PL-15-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Quadrant EPP TIVAR® 1000 Black Virgin	Quadrant Engineering Plastic Products	UHMWPE	Quadrant EPP
Sinvicomp SIZ4809	Teknor Apex Asia Pacific PTE. LTD.	PVC, Rigid	Sinvicomp
YUNGSOX® PP 1600D	Formosa Polypropylene	PP Homopolymer	YUNGSOX® PP
Flontech® FT-BRR30-8	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
KOCETAL® GB305	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®